Abstract: The electrochemical behavior of film and charge-discharge capacity of Li-ion cell in 1 M LiPF6/EC:DME
(1 : 1, by volume ratio) electrolyte solution was studied using chronopotentiometry, cyclic voltammetry, chronoamperometry, and impedance spectroscopy. The first irreversible capacity was higher than the second irrversible capacity because of solvent decomposition. Especially, passivation film that is electron insulating and ionic conducting were formed on the MPCF by solvent decomposition during the first charge. The solvated Li is co-intercalated with solvent into MPCF electrode. Part of the MPCF is expoliated during co-intercalation of solvent-Li. The MPCF ends up nonuniformly covered by a relatively thick layer of exfoliated particles embedded in a matrix of product by solvent decomposition.
Keywords: #Li-ion battery #Charge-discharge capacity #Solvent decomposition #Intercalation/deintercalation
|